Chemical Composition ( IN PERCENTAGE )

Stainless Steel

Grade
C (Max)
Mn (Max)
P (Max)
S (Max)
Si (Max)
Cr
Ni
Mo
Nitrogen (Max)
Cu/ Others
301
0.15
2.00
0.045
0.030
1.00
16.00 – 18.00
6.00 – 8.00
-
0.10
-
304
0.08
2.00
0.045
0.030
0.75
18.00 – 20.00
8.00- 10.50
-
0.10
-
304L
0.030
2.00
0.045
0.030
0.75
18.00 – 20.00
8.00- 12.00
-
0.10
-
310S
0.08
2.00
0.045
0.030
1.50
24.00- 26.00
19.00 – 22.00
-
-
-
316
0.08
2.00
0.045
0.030
0.75
16.00 – 18.00
10.00 – 14.00
2.00 – 3.00
0.10
-
316L
0.030
2.00
0.045
0.030
0.75
16.00 – 18.00
10.00 – 14.00
2.00 – 3.00
0.10
-
317
0.08
2.00
0.045
0.030
0.75
18.00 – 20.00
11.00 – 14.00
3.00 – 4.00
0.10
-
317L
0.030
2.00
0.045
0.030
0.75
18.00 – 20.00
11.00 – 15.00
3.00 – 4.00
0.10
-
321
0.08
2.00
0.045
0.030
0.75
17.00 – 19.00
9.00 – 12.00
-
0.10
Ti5 ( C + N ) Min or 0.70 max
347
0.08
2.00
0.045
0.030
0.75
17.00 – 19.00
9.00 – 13.00
-
-
Cb= 10x ( C Min ) or 1.00 Max
409
0.08
1.00
0.040
0.010
1.00
10.50 – 11.75
0.50
-
-
Ti= 6x (C+ N ) Min or 0.70 Max
409M
0.03
0.81.2
0.030
0.030
0.40.75
11.00- 12.00
1.5 max.
-
-
Ti= 6x (C) Min or 0.70 Max
410S
0.08
1.00
0.040
0.030
1.00
11.50- 13.50
0.60
-
-
-
410
0.15
1.00
0.040
0.030
1.00
11.50- 13.50
0.75
-
-
-
420
0.35
0.50
0.035
0.015
0.50
12.00 – 13.00
0.20.3
-
-
-
430
0.12
1.00
0.040
0.030
1.00
16.00 – 18.00
0.75
-
-
-
JSL AUS
0.08
7.08.0
0.070
0.030
0.75
15.50 – 16.50
4.25 – 4.75
-
-
0.9 – 1.10
JS- 203
0.08
9.2510.25
0.070
0.030
0.75
14.25 – 15.25
2.25 – 2.75
-
-
1.60- 2.0
301M
0.10
4.55.5
0.060
0.030
0.75
14.50 – 15.50
6.0 – 7.0
-
-
1.70- 1.90
* Thickness of 1.27mm & below will have elongation of 20% min.

 

ALLOY STEEL

Chemical Composition,%

Tensile Test

Designation
C max.
Si
P max
S max
Tensile Strength Kgf/mm2
Yield Point Kgf/mm2,min.
Elongation
Test Piece
%, min
IS 2002-1
0.18
.010-0.35
0.40
0.40
37-45
55
5.65/So
4/So
26
30
IS 2002-2A
0.20
0.10-0.35
0.050
0.050
42-50
50
5.65/So
4/So
25
29
IS 2002-2b
0.22
0.10-0.35
0.050
0.050
52-62
50
5.65/So
4/So
20
24

 

Kawasaki Specification [AG] Steel Plates for Galvanizing Pots

Chemical Composition,%

Tensile Test

Bend test

Designation
C    Si    Mn     P   S
Max       Max        Max
Yield Point      Tensile Strength
Kgf/mm2        Kgf/mm2.(N/mm2)
Elongation
%, Test Piece
Angle of Bend
Inside Radius
AG
0.09 tr.0.20-0.40 0.30 0.030
–                           –
–                  –

 

ASTM A 285-78 Pressure Vessel Plates, Carbon Steel, Low – and Intermediate- Tensile Strength

Chemical Composition,%

Tensile Test*1

1. (i) Refer to  (1) for ASTM A 203

(ii) Refer to (2) for ASTM A 203

(iii) Refer to (4) for ASTM A 203.

Designation
C max
Mn max
P max
S max
Tensile Strength
ksi (MPa),
Yeild Strengh ksi(MPa),min.
Elongation,% min

GL=8 in.
GL=2 in

A 285 A
0.17
0.90
0.035
0.040
45-65 (310-450)
24(165)
27              30
A 285  B
0.22
0.90
0.035
0.040
50-70(385-485)
27(185)
25
28
A 285 C
0.28
0.90
0.035
0.040
55-75(380-515)
30(205)
23              27